Acondicionamiento con ácido fosfórico al 37% en esmalte y dentina a diferentes tiempos de grabado y su influencia en la adhesión: estudio invitro en premolares extraídos por medio de resistencia a la tracción
- Authors
- Puente Armas, Mayra Alejandra
- Format
- BachelorThesis
- Status
- publishedVersion
- Description
En el proceso adhesivo el grabado ácido proporciona irregularidades a las superficies de esmalte y dentina creando microretenciones para recibir al adhesivo.El objetivo de este estudio fue analizar el acondicionamiento del ácido fosfórico al 37% en esmalte y dentina a diferentes tiempos de grabado y su influencia en la adhesión mediante resistencia a la tracción. Se seleccionaron 45 premolares, manteniéndoles en suero fisiológico. Se sumergieron las piezas en bloques de acrílico, luego se cortó a nivel oclusal. Se conformaron bloques de resina (Z350XT 3M) alrededor de un tornillo. Aleatoriamente se distribuyeron en tres grupos de 15 piezas cada uno aplicándoles al esmalte y dentina ácido fosfórico al 37% (scothbond 3M). Grupo 1: 60 y 15segundos. Grupo 2: 30 y 10segundos. Grupo 3: 15 y 5segundos, respectivamente. A cada grupo se aplicó el adhesivo (single bond 2 3M). Finalmente se sometieron las probetas a la prueba de tracción. Los resultados obtenidos fueron para el: Grupo 1: 3,85MPA, Grupo 2: 5,86 MPA y Grupo 3: 6,67 Mpa estableciéndose diferencias estadísticas significativas en los tres grupos. Se concluye que la aplicación del ácido fosfórico al 37% durante 15 segundos en esmalte y 5 en dentina permitió obtener la mayor resistencia adhesiva
In the adhesive process the acid engraved provides irregularities on the surfaces of enamel and dentine creating microretentions to receive the adhesive. The objective of this study was to analyze the conditioning of the phosphoric acid to the 37% in enamel and dentine at different times of engraving and its influence in the adhesion through resistence to the traction. It was selected forty five premolars, keeping them in physiological saline. the pieces were immersed in blocks of acrylic, then they were cut at oclusal level. It was formed blocks of resin (z350XT 3M) about one screw. Randomly It was formed three groups of fifteen pieces each one by applying to the enamel and phosphoric acid dentin to the 37% (scothbond 3M). Group 1:60 and 15 seconds. Group 2:30 and 10 seconds.Group 3: 15 and 5 seconds, respectively. To each group it was applied the adhesive (single bond 2 3M). Finally it was subjected the test tubes to the traction test. The obtained results were for the : Group 1:3,85 MPA, Group 2: 5,86 MPA and Group 3: 6,67 MPA establishing statistically meaningful differences in the three groups. It is concluded that the application of the phosphoric acid to the 37% during 15 seconds in enamel and 5 in dentin allowed to obtain the major adhesive resistence
- Publication Year
- 2015
- Language
- spa
- Topic
- ÀCIDO FOSFÒRICO
INFLUENCIA EN LA ADHESIÓN
TIEMPOS DE GRABADO
ESMALTE
PREMOLARES EXTRAÌDOS
RESISTENCIA A LA TRACCIÒN
DENTINA
- Repository
- Repositorio de la Universidad Central del Ecuador
- Get full text
- http://www.dspace.uce.edu.ec/handle/25000/3562
- Rights
- openAccess
- License
- http://creativecommons.org/licenses/by-nc-sa/3.0/ec/